DIN 2.0882 Material


Exporter of DIN 17664, ASTM B 151/122/171 C70600, 2.0882 cuni, Check CuNi30Mn1Fe, CW 354H Price list in India





What is DIN 17664 W No 2.0882


AGL Pipe stocks and sell DIN 2.0882 AMS 2750D-Round Bar, as a india's biggest & oldest stockist of Copper nickel alloy we provice CuNi material as per DIN 17664 standards, we have wide thickness in DIN 2.0882 AMS 2750D - Wire, buy 2.0882 cuni products at best price in India, we are supplier, stockist & exporter of Wrought copper alloys in India, at AGL Pipe check price list of 
Din 2.0882 Ams 2750d Sheet, DIN 2.0882 & DIN 17664 are standards of Wrought copper alloys/ copper-nickel alloys, 

equivalent grades of DIN EN 2.0872 material also known as C70600. we have wide range of Alloy C70600 fasteners, you can replace alloy c70600 bolts at best price in India at AGL Pipe, mail to admin@aglpipe.com for Alloy C70600 screws price list,

we can also provide online price of Alloy c70600 stud bolts, alloy c70600 threaded rod, c70600 nuts in various types & threads

Copper Nickel Pipe, Tube, Sheet, Plates for light-duty condensers, sugar-making and desalination plants, including power stations, feed water heaters and evaporators. The addition of nickel to copper improves strength and corrosion resistance but good ductility is retained. DIN 17664, DIN 2.0882, copper nickel alloys, composition, DIN 17664-1, Copper-nickel wrought alloys. CuNi30Mn1Fe, 2.0882 Price in India.



DIN 17664, 2.0882 Chemical Composition


ElementCuNiMnFeImpurities
%Bal30-320.5-1.50.6-1.00.3 Max

DIN 2.0882 Mechanical Properties


FormCross sectional area
Metric mm
Yield 0.2% MPaUTS 
MPa
Elong %Izod (Joules)
Rod>180-500120-140330-36034-4054-90
Rod>500-1230115-135320-35032-3854-85
Rod>1230110-130310-25030-3654-85
ForgingsAll sizes110-140310-36030-4054-100

W Nr 2.0882 Physical Properties


(Courtesy Def Stan 02-879)
MetricImperial
Density8950 kg/m³0.325lb/in³
Specific Gravity8.95
Specific Heat377J/kg K0.09Btu/lb°F
Electrical Conductivity2.7m/Ω-mm²@20 ºC5% IACS
Thermal Conductivity29.3 W/mK17Btuft/ft²hr°F
Thermal Linear Expansion16 µstain/K Range (20-200 ºC)9x 10-6per°F Range (68-572°F)
Electrical Resistivity0.34 Ωmm²/m207Ω(circ mil/ft
Relative Magnetic Permeability1.0006 µ
Machining Index20% (Based on free machining brass 100%)
Modulus of Rigidity (50mm rod annealed)57 GPa
Modulus of Elasticity (50mm rod annealed) (In Tension)152 GPa
Shear Strength (50mm rod annealed)205MPa
Poisson’s Ratio0.33
Fatigue Limit in air (rotating)(25mm rod)1x107 cycles +/- MPa 154
Melting Range1170-1240 ºC2140-2265°F
Hot Working925-1025ºC (No forging below 850 ºC)1695-1875°F
Cold Workinggood (Anneal 650-850 ºC)1200-1560°F
CryogenicRetains properties down to -269 ºC-516°F
Elevated TemperaturesRetains properties to 350 ºC662°F

Ranges of Manufacturing


» Available in square, rectangle, rod, bar, plate, hollow and all shaped forgings up to 4,500kgs (9900lbs).

» AGL Pipe also offers finished machined components in all alloys, complete project management and tailored mechanical properties     beyond those of the specification to meet special customer requirements.

» Copper Alloys is also regularly making customised shaped forgings and can increase piece weight up to 20,000kg/44,000lbs.